| Electrospun Fibers of PLA/ENR Blends : Effect of Nanofiller Addition on Thermal Properties |
| 關鍵詞： |
PLA/ENR blend Nanocomposite Electrospinning Thermal properties |
| 類 別： |
塑料 >> 塑料加工 |
| 來 源： |
第六亞歐研討會上處理和性能增強聚合物會議文集（2013.6.2-6 武漢） |
| 資料類型： |
pdf文件 |
| 資料大小： |
72K |
| 簡 介： |
This study deals with the preparation of electrospun fibers of poly (lactic acid) (PLA)/expoxidized natural rubber (ENR) blends added with nanofillers using electrospinning technique.The electrospun PLA/ENR/nanofiller fibers were characterized by SEM. The effect of nanofiller addition on the thermal properties of PLA/ENR fibers was then studied using DSC and TGA
techniques. The various ratios of 10 wt% PLA and 3 wt% ENR in chloroform solution with and without nanofillers (Si02 and Ti02 nanoparticles) were mixed and stirred homogeneously for 40 min before spinning. The SEM images showed that the nanocomposite fibers showed a porous morphology with a diameter ranged from 3-15 ym. From DSC results, all electrospun fibers exhibited a significant lower Tg than that of pure PLA (61 0C)cl] , implying the partial miscibility of the electrospun PLA/ENR fibers. Also, crystallization temperature ( Tc) was found in all blends fibers suggesting the enhancement of crystallization ability of PLA due to the presence of ENR. Thermal stability of most PLA/ENR blend fibers was slightly less than that of pure PLA fiberc2].
Interestingly, electrospun fibers of PLA/ENR (8 : 2) incorporating with 0. I wt% Si02 nanofiller exhibited a significant improvement in thermal stability. However, addition of Ti02 had no remarkable effect on thermal stability of the nanocomposites fibers. |
| 上傳人： |
liu |
| 上傳時間： |
2013-06-25 11:20:39 |
| 下載次數： |
1 |
| 消耗積分： |
2 |
| 我要收藏： |
 |
| |
友情提示：下載后對該資源進行評論，即可獎勵2分。 |
|
本欄目部分資源來自互聯網，僅為促進數據共享和信息交流，如有版權問題請告知本網或上傳者本人，本網會及時給予答復。 |
| 報告錯誤
1.下載無效
2. 資料明顯無價值
3. 資料重復存在
|