[Composites Part A]Synchronously improved electromagnetic interference shielding and thermal conductivity for epoxy nanocomposites by constructing 3D copper nanowires/thermally annealed graphene aerogel framework
作者：Xutong Yang, Shuguang Fan, Ying Li*, Yongqiang Guo, Yunge Li, Kunpeng Ruan, Shengmao Zhang, Junwei Gu
關鍵字：copper nanowires, thermally annealed graphene aerogel
論文來源：期刊
具體來源：Composites Part A: Applied Science and Manufacturing
發表時間：2019年
3D copper nanowires-thermally annealed graphene aerogel (CuNWs-TAGA) framework is firstly prepared by freeze-drying followed by thermal annealing from CuNWs, graphene oxide (GO) and L-ascorbic acid. Epoxy resin is then poured back into the above 3D CuNWs-TAGA framework to fabricate the CuNWs-TAGA/epoxy nanocomposites. CuNWs with average diameter of about 120?nm and length of approximate 10?μm are successfully prepared. When the mass fraction of CuNWs-TAGA is 7.2 wt% (6.0–1.2 wt% CuNWs-TAGA), the thermal conductivity coefficient (λ) value of the CuNWs-TAGA/epoxy nanocomposites reaches the maximum of 0.51 W/mK. Meantime, the CuNWs-TAGA/epoxy nanocomposites exhibit the maximum electromagnetic interference shielding effectiveness (EMI SE) value of 47?dB and electrical conductivity (σ) of 120.8 S/m, ascribed to perfect 3D CuNWs-TAGA conductive network structures. Meanwhile, the corresponding elasticity modulus, hardness, glass transition temperature (Tg) and heat-resistance index (THRI) of the CuNWs-TAGA/epoxy nanocomposites increase to 4.69? GPa, 0.33? GPa, 126.3°C and 181.7°C, respectively.