Synthesis and characterization of 4. trans-1,4-poly(butadiene-co-isoprene) rubbers (TBIR) with different fraction and chain sequence distribution and its influence on the properties of natural rubber/TBIR/carbon black composites
作者：Weitian Li, Wei Peng, Shuting Ren, Aihua He*
關鍵字：Trans-1,4-poly(butadiene-coisoprene) rubbers，
論文來源：期刊
發表時間：2019年
Higher performance tire tread stocks with lower rolling resistance, higher abrasion, and fatigue resistance are urgent needs considering environmental protection, resource saving, and personal safety. In this paper, high trans-1,4-poly(butadiene-co-isoprene) copolymer rubbers (TBIR) consist of three main fractions containing trans-1,4-polyisoprene (TPI) blocks and/or trans-1,4-polybutadiene (TPB) blocks with varied sequence length and butadiene content, which have varied crystalline and degradation behavior. Blending 10 phr TBIR with natural rubber (NR) in a truck tire tread stock, the vulcanizated NR/TBIR/carbon black (CB) composites present improved modulus at 300% and abrasion resistance, higher fatigue resistance, lower rolling resistance, and heat buildup. The contribution of the TBIR fraction distribution on the properties of the improved fatigue resistance for NR/TBIR/CB composites are discussed. NR/TBIR-1/CB vulcanizate with satisfied comprehensive properties and acceptable tear strength reveals that the fraction and chain sequence distribution of TBIR do have an obvious influence on the final performance of the composites.