Journal of Macromolecular Science Part A: Pure and Applied Chemistry 2009, 46, 1103–1113
作者：Jiashi Li, Yan Zhang, Jie Chen, Chaohua Wang, and Meidong Lang*
關鍵字：Poly(ε-caprolactone), 5-FU, nanoparticle, carboxyl groups
論文來源：期刊
發表時間：2009年
In this paper, 5-Fluorouracil (5-FU) loaded carboxylic poly(ε-caprolactone) nanoparticles have been prepared by emulsification/solvent evaporation o/w method, and the drug release behaviors of 5-FU were investigated. The novel carboxylic poly (ε-caprolactone) (P(CL-OPD)-mal) was synthesized via conjugation of maleic anhydride to sodium borohydride (NaBH4) reduced poly(ε-caprolactone-co -4- carbonyl -ε-caprolactone) (P(CL-OPD)), while P(CL-OPD) was synthesized in bulk by ring-opening polymerization of ε-caprolactone and 4-carbonyl-ε-caprolactone (OPD) with stannous octoate as a catalyst. Their structures were confirmed by 1HNMR, FT-IR and GPC. Dynamic light scattering (DLS), transmission electron microscopy (TEM), zeta potential measurements were used for nanoparticle characterization. TEM and DLS showed the nanoparticles were with spherical shape and uniform size distribution (mean diameter 70∼100 nm), respectively. Zeta potential analysis revealed that the nanoparticles had an increased negative surface with the increase of carboxyl group concentration. UV spectroscopy was adopted to study the entrapment and release behaviour. The maximum 5-FU loading efficiency was 14.39% with the entrapment efficiency be 42%. In vitro release studies were performed in PBS at 37?C. Results of the study showed that the release behavior can be well-controlled, and the balanced release was up to 96 h. P(CL-OPD)-mal nanoparticles would provide increased benefit in biomedical and pharmaceutical applications.