作者：Xie Qin, Liu Zhaoping, Shao Mingwang, Kong Lingfen, Yu Weichao, Qian Yitai*
關鍵字：Crystal morphology, Hydrothermal crystal growth; A2. Single crystal growth, Nanomaterials, Polymers, Semiconducting materials
論文來源：期刊
具體來源：J. Crystal Growth 2003, 252, 570-574.
發表時間：2003年
Sb2Se3 nanoribbons have been prepared by a hydrothermal process at 180°C for 20 h. X-ray diffraction pattern indicates that the product was orthorhombic Sb2Se3 phase with lattice constants a=11.747, b=11.799 and c=3.987 Å. Field emission scanning electron microscope images show that nanoribbons have diameters in the range of 25–100 nm and lengths up to 
30 μm. High-resolution transmission electron microscopy image reveals that the nanoribbon was of single crystal and grew along the [0 0 1] direction. The peak of absorption appeared at 727 nm in the UV-vis spectrum. A possible mechanism on the formation of the nanostructures was also discussed.