9. "DSC and TMDSC Study of Melting Behaviour of Poly(butylene succinate) and Poly(ethylene succinate)". Qiu ZB,* Komura M, Ikehara T, and Nishi T.* Polymer 2004; 44: 7781-7785.
The subsequent melting behaviour of poly(butylene succinate) (PBSU) and poly(ethylene succinate) (PES) was investigated using DSC and TMDSC after they finished nonisothermal crystallization from the melt. PBSU exhibited two melting endotherms in the DSC traces upon heating to the melt, which was ascribed to the melting and recrystallization mechanism. However, one melting endotherm with one shoulder and one crystallization exotherm just prior to the melting endotherm were found for PES. The crystallization exotherm was ascribed to the recrystallization of the melt of the crystallites with low thermal stability, and the shoulder was considered to be the melting endotherm of the crystallites with high thermal stability. The final melting endotherm was ascribed to the melting of the crystallites formed through the reorganization of the crystallites with high thermal stability during the DSC heating process. TMDSC experiments gave the direct evidences to support the proposed models to explain the melting behaviour of PBSU and PES crystallized nonisothermally from the melt.