ACS Sustainable Chemistry & Engineering——Co-depositing mussel-inspired nanohybrids onto 1D fibers under “green” conditions for significantly enhanced surfacial/interfacial properties
作者：Xiaobing Yang，Hongpeng Du，Songwei Li，Zhenxing Wang，Lu Shao
關(guān)鍵字：Mussel-inspired coatings
論文來源：期刊
具體來源：ACS Sustainable Chemistry & Engineering
發(fā)表時(shí)間：2018年
Co-deposition of mussel-inspired nanohybrid coating was realized onto carbon fiber (CF) surface via co-incubation in the dopamine (DA) and octaammonium polyhedral oligomeric silsesquioxane (POSS-NH2) mixed aqueous solution. The deposition procedure was conducted under ambient conditions, and no harsh conditions and toxic solvents were needed. The surface morphology, compositions, and energies of CFs were investigated. The interfacial shear strength (IFSS) were measured to demonstrate the interfacial combination and compatibility of fiber and epoxy resin, and the single-filament tensile strength (TS) was also determined to evaluate the damage degree brought by the modification procedure to the fiber intrinsic strength. As a result, the nanohybrid coating could greatly enhance surface wettability, interfacial compatibility, and interfacial mechanical strength, and bring no deterioration to fiber intrinsic strength. Our facile strategy presents a promising platform to modify various 1D fiber surface for advanced composite materials towards broadly mechanical-demanding and energy-saving usages.