Biobased poly(butylene 2,5-furandicarboxylate) and poly(butylene adipate-co-butylene 2,5-furandicarboxylate)s: From synthesis using highly purified 2,5-furandicarboxylic acid to thermo-mechanical properties
作者：Binshuang Wu, Yutao Xu, Zhiyang Bu, Linbo Wu*, Bo-Geng Li, Philippe Dubois.
關鍵字：biobased, biodegradable, polyester, furandicarboxylic acid
論文來源：期刊
具體來源：Polymer, 55(16): 3648-3655,
發表時間：2014年
To synthesize high quality (co)polyesters derived from 2,5-furandicarboxylic acid (FA), an acetic acid refluxing/pH-swing method was proposed to purify FA. 2-Carboxyl furfural and other impurities were removed completely from FA with this method. Using highly purified FA, biobased polyester poly(butylene furnadicarboxylate) (PBF) and aliphatic-aromatic copolyesters poly(butylene adipate-cobutylene 2,5-furandicarboxy-late)s (PBAFs) were synthesized via melt (co)polycondensation. The (co) polyesters were characterized with GPC, FTIR, 1H NMR, DSC and TGA, and their tensile mechanical properties were also assessed. The copolyesters possess random chain structure, monomer feed ratiocontrolled copolymer composition and excellent thermal stability (Td,5% > 340 C) in full composition range. Both BA-rich and BF-rich PBAFs are crystalline polymers. The crystallizability decreases with composition, up to nearly amorphous at moderate fBF (40e60%). PBAFs with fBF no more than 50% exhibit obvious high-elastic deformation and rebound resilience, and possess tensile properties (E 18-160 MPa, sb 9-17 MPa, εb 370-910%) comparable to poly(butylene adipate). PBAFs with higher fBF behave like nonrigid plastics with low tensile moduli (42e110 MPa), moderate strength (30e42 MPa) and high elongation at break (310e470%). In comparison, PBF is a strong and tough thermoplastic having balanced mechanical properties, namely, much higher tensile modulus (1.9 GPa) and strength (56 MPa) and high elongation at break (260%). It seems necessary and effective to use highly purified FA for synthesizing high performance FA-derived (co)polyesters.