作者：Dong Tungalag, Yu Zhenfei, Wu Jiaxin, Zhao Zilong, Yun Xueyan, Wang Yu, Jin Ye, Yang Jinjun
關鍵字：Thermal property, Barrier property, Poly(L-lactide)
論文來源：期刊
具體來源：Polymer Science, Series A
發表時間：2015年
In this study, both stretched and annealed polylactide (PLA) films were prepared by a twin!screw extruder with different draw ratios, and the effects of the orientation, crystallization, ambient temperature and humidity on the barrier properties were evaluated. The wide!angle X!ray diffraction results revealed that the crystallinity increase with the increase of draw ratio, and the α''!crystal was produced by uniaxially stretching. Moreover, the α''!crystal was easy to form when the film was annealed at 90°C. Based on the scanning electron microscopy observation, the film surface cracks occurred at a certain draw ratio. Modulated differ! ential scanning calorimetry (MDSC) results showed that the glass!transition temperature and crystallinity increased with the increase of draw ratio. The barrier behavior results showed that, both stretched and annealed PLA films exhibited much better oxygen and water vapor barrier than undrawn PLA at middle draw ratio. Upon further stretching, their barrier ability was reduced. The annealed PLA film had higher barrier ability than that of the stretched PLA film. With regard to the temperature and humidity, the oxygen perme! ability coefficient increased with the increase of temperature, however, the water vapor permeability coefficient reduced slightly. The oxygen and water vapor permeability coefficient were insensitive to humidity.