Preparation of Monodisperse Crosslinked Polymer Microspheres Having Chloromethyl Group by Distillation-precipitation Polymerization
作者:Shu-feng Li, Xin-lin Yang, Wen-qiang Huang*
關鍵字:Chloromethylstyrene; Divinylbenzene; Distillation-precipitation polymerization; Crosslinked; Monodisperse;
論文來源:期刊
具體來源:Chin. J. Polym. Sci. 23 (2), 197-202 (2005).
發表時間:2005年
Monodisperse crosslinked poly(chloromethylstyrene-co-divinylbenzene) (poly(CMSt-co-DVB)) microspheres were prepared by distillation-precipitation copolymerization of chloromethylstyrene (CMSt) and divinylbenzene (DVB) in neat acetonitrile. The polymer particles had clean surfaces due to the absence of any added stabilizer. The size of the particles ranges from 2.59 μm to 3.19 μm and with mono-dispersity around 1.002?1.014. The effects of monomer feed in copolymerization on the microsphere formation were described. The polymer microspheres were characterized by SEM and chlorinity elemental analysis.
關鍵字:Chloromethylstyrene; Divinylbenzene; Distillation-precipitation polymerization; Crosslinked; Monodisperse;
論文來源:期刊
具體來源:Chin. J. Polym. Sci. 23 (2), 197-202 (2005).
發表時間:2005年
Monodisperse crosslinked poly(chloromethylstyrene-co-divinylbenzene) (poly(CMSt-co-DVB)) microspheres were prepared by distillation-precipitation copolymerization of chloromethylstyrene (CMSt) and divinylbenzene (DVB) in neat acetonitrile. The polymer particles had clean surfaces due to the absence of any added stabilizer. The size of the particles ranges from 2.59 μm to 3.19 μm and with mono-dispersity around 1.002?1.014. The effects of monomer feed in copolymerization on the microsphere formation were described. The polymer microspheres were characterized by SEM and chlorinity elemental analysis.