Temperature dependence of surface composition and morphology in polymer blend film.
作者：Jichun You, Tongfei Shi, Yonggui Liao, Xinglin Li, Zhaohui Su, Lijia An.
關鍵字：Polymer 2008, 49: 4456-4461.
論文來源：期刊
Thin films of poly(methyl methacrylate) (PMMA) and poly(styrene-ran-acrylonitrile) (SAN) blend can phase separate upon heating to above its critical temperature. Temperature dependence of the surface composition and morphology in the blend thin film upon thermal treatment was studied using in situ X-ray photoelectron spectroscopy (XPS) and in situ atomic force microscopy (AFM). It was found that in addition to phase separation, the blend component preferentially diffused to and aggregated at the surface of the blend film, leading to the variation of surface composition with temperature. At 185 C, above the critical temperature, the amounts of PMMA and SAN phases were comparable. At lower temperatures PMMA migrated to the surface, leading to a much higher PMMA surface content than in the bulk. The migration and preferential segregation of a blend component in thin films demonstrated here are responsible for the great difference between in situ and ex situ experimental (not real quenching or annealing) results of polymer blend films, and help explain the slow kinetics of surface phase separation at early stage for blend thin films reported in literature. This is significant for the control of surface properties of polymer materials.