【Materials Letters】Tunable field emission properties of carbon nanotube arrays by engineering Fe catalysts
作者：Bin Zhao, Zhenlun Song, Junhe Yang
關鍵字：Carbon nanotubes, field emission
論文來源：期刊
具體來源：Materials Letters, 2009, 63: 2556–2559.
發表時間：2009年
High-quality carbon nanotube (CNT) arrays composed of nanotubes with different diameters and wall numbers were synthesized by water-assisted chemical vapor deposition (CVD) from engineered Fe catalysts. Interestingly, the distribution of nanotube diameter and wall number broadened over 2.5 times as the catalytic Fe thickness increased. The mean diameter and wall number of nanotubes increased monotonically with the Fe thickness, while the calculated CNT area density within an array dropped about 32 times. Field emission measurements revealed that the turn-on voltage for CNT arrays decreased from 3.5 to 2.5 V/μm with the increased catalytic Fe thickness. It was believed that the screening effect from the proximity of neighboring nanotubes has a dominant influence than the CNT diameter on the resulting turn-on voltage.