Mechanically strengthened Polyamide 66 nanofibers bundles via compositing with polyvinyl alcohol
作者：Shasha Wu, Guoqiang Zheng(通訊作者), Xiaoyang Guan, Xingru Yan, Jiang Guo,Kun Dai, Chuntai Liu, Changyu
關(guān)鍵字：polyvinyl alcohol
論文來(lái)源：期刊
具體來(lái)源：Macromolecular Materials ＆ Engineering, 2016, 55, 212-219
發(fā)表時(shí)間：2016年
Electrospun polyamide PA 66 nanofiber bundles were mechanically strengthened via compositing with polyvinyl alcohol (PVA). The highest tensile strength (126.4 MPa) was achieved for the bundles immersed in the solution with 5.0 wt% PVA, indicating sufficient PVA filling between nanofibers after drying the impregnated nanofiber bundles. The disappearance of voids for the bundles immersed in the PVA solution indicated a superb interface adhesion, which was responsible for the excellent mechanical properties of the composite bundles. Furthermore, the step-cycle and stress relaxation tests were carried out to shed light on the deformation evolution and the viscous stress of the bundles. The results further demonstrated the excellent mechanical properties of the composite bundles.